8406-20G CHEMTOOLS 8406 Wicking Grade Adhesive Low Viscosity 20Ml Meets Military Specification Mlla 46050 Type Ii Class Ii 8406 WICKING GRADE

20ml ChemTools 8406 Cyanoacrylate Adhesive - Low Viscosity, Fast Cure Speed

Instant Adhesive 8406

Cyanocrylate adhesives offer a major advantage over other types of adhesive systems. They are a single componentadhesive, fast curing at room temperature, solvent free and resistant to many environmental factors.

FEATURES:

CHEMTOOLS 8406 is low viscosity combined with fast curespeed, surface insensitive cyanoacrylate adhesive (CA). It is specifically formulated to bond difficult surfaces with high industrial strength..

Ideal for bonding rough, porous and acidic surfaces including Wood, Cardboard, Balsa Wood, Rubbers, Plastics, Metals, Leather, etc.

Wide variety of industrial manufacturing and repairingapplications

Meets Military specification MLLA 46050 Type II Class II

• One part adhesive
• Solvent free
• Fast curing at room temperature
• High Tensile shear strength
• Surpasses most other types of adhesives for bonding rubbers.

APPLICATIONS:

• Ideal for bonding rough, porous and acidic surfaces including Wood, Cardboard, Balsa Wood, Rubbers, Plastics, Metals, Leather, etc.
• Wide variety of industrial manufacturing and repairing applications

BONDING TIMES:

• Plastics 2-5 seconds
• Rubbers < 3 seconds
• Wood 1-5 seconds
• Leather 5-15 seconds
• Metals 8-10 seconds
• Ceramics 12-18 seconds

PHYSICAL PROPERTIES:

• Liquid
• Composition Ethyl Cyanoacrylate
• Appearance Colorless liquid
• Viscosity@ 25C 20 cps
• Brookfield LVT Spindle 1@ 30 rpm
• Cured Adhesive
• Gap Filling 0.05mm
• Tensile Shear Strength 18-28 n/mm2
• Service Temperature Range -60 to +80C
• Full Cure 24 hours
• Melting Point Temperature 160 to 170C

Shear Strength ASTM D 1002/DIN 53283

• Grit Blasted Steel >20 N/mm2
• Etched Aluminum >18 N/mm2
• Rubbers >22 N/mm2
• Wood >25 N/mm2
• Polycarbonate >12 N/mm2
• ABS >10 N/mm2

Mechanical Properties:

• Coefficient of thermal conductivity, ASTM C177, W.m-1 k-1 0.1
• Glass Transition Temperature, ASTM E228, 122C
• Coefficient of thermal expansion, ASTM D696, K-1 75x 10-6
• Dielectric strength, ASTM D149, kV/mm 27
• Volume resistivity, ASTM D257, Ohm.cm 1 x 1016
• Dielectric constant, 25 C, ASTM D150 2.7

APPLICATION INSTRUCTIONS

• All surfaces must be clean, dry, dust and grease free. Best result will be achieved with surfaces that have been lightly abraded immediately prior to bonding.
• If using accelerator apply to one component surfaceonly. Apply thin film of adhesive to the other surface and bring the pieces together immediately. Hold for few seconds without disturbing the joints.
• When bonding "O" rings, cut a fresh surface onto each end of the rubber to gain the best possible strength.

Weight: 0.0320